Polyether type composite A-1014F-1/B-5009
Characteristic: Low density and hardness, high rebound
Application: Insole
Typical properties of PU matrix
Name of products | Appearance | Viscosity (mPa·s/40℃) | Density （g·cm-3/40℃） | Package (kg) |
| A-1014F-1 | Cream white liquid | 600~800 | 1.01~1.02 | 18 |
| B-5009 | Yellowish transparent liquid or waxy | 400~600 | 1.08~1.20 | 20 |
Typical processing parameters & Reaction parameter
ltems | AB Materials Temperatures (℃) | A+C+120gH2O/B Mix ratio (By weight) | Cream Time (s) | End of Rise Time (s) | Free Rise Foam Density(g/cm3) | Mold Temperature (℃) | Demold Time (min) |
Parameter | 30~35/35~40 | 100/40~55 | 6~8 | 45~55 | 0.13~0.16 | 45~55 | 4~5 |
Physical properties
ltems | Molded Density (g/cm3) | Hardness (Shore C ) | Tensile strength (MPa) | Elongation (%) | Rebound (%) | Tear Strength (kN/m) | Adhesive N/cm | Compr- ehension 6H % |
Physical properties | 0.27~0.32 | 25~32 | 0.6~0.8 | 270~300 | 35-38 | 5~7 | 0.4~0.6 | 3~5 |
Polyether type composite material A-1014T/B-5301T
Characteristic: Mold does not require heating
Application: Insole
Typical properties of PU matrix
Name of products | Appearance | Viscosity (mPa·s/40℃) | Density （g·cm-3/40℃ | Package (kg) |
| A-1014T | Cream white liquid | 600~800 | 1.01~1.02 | 18 |
| B-5009 | Transparent liquid | 400~600 | 1.08~1.20 | 20 |
Typical processing parameters & Reaction parameter
ltems | A/B Materials Temperatures (℃) | A+C+60gH2O/B Mix ratio (By weight) | Cream Time (s) | End of Rise Time (s) | Free Rise Foam Density(g/cm3) | Mold Temperature (℃) | Demold Time (min) |
Parameter | 30~35/35~40 | 100/40~55 | 6~8 | 35~45 | 0.12~0.17 | 4~5 | 5~7 |
Physical properties
ltems | Molded Density (g/cm3) | Hardness (Shore C ) | Tensile strength (MPa) | Elongation (%) | Rebound (%) | Tear strength N/cm |
Physical properties | 0.27~0.35 | 25~40 | 0.5~0.8 | 220~270 | 37~43 | 7~9 |